PP Melt Grade

Polypropylene Ultra Low Melting Index
PP 超低熔融值
Property
物性
Test Methodbr
測試方式
Unit
單位
Value
數值
Melt Flow Index
熔融指數
ASTM D-1238   230oC x 2.16kg g/10min 6
Tensile Strength at Yield
拉力降伏強度
ASTM D-638     23oC kg/cm2 360
Tensile Strength at Break
拉力斷裂強度
ASTM D-638     23oC % 14
Flexural Modulus
彎曲模數
ASTM D-790A     23oC kg/cm2 18000 
Hardness
硬度
ASTM D-785     23oC R-Scale 98
Izod Impact Strength
衝擊強度
ASTM D-256     23oC kg-cm/cm 3.6
Melting Point
熔點

ASTM D-648 at 4.6kg/cm
Unannealed1/4"

oC 99
Molding Shrinkage
縮收率
FCFC     23oC %  1.3
Specific Gravity
比重
ASTM D-792    23oC/23oC   0.905

Typical properties can be subject to change without further notice

Polypropylene High Melting Index
PP 高熔融值
Property
物性
Test Methodbr
測試方式
Unit
單位
Value
數值
Melt Flow Index
熔融指數
ASTM D-1238   230oC x 2.16kg g/10min 15
Tensile Strength at Yield
拉力降伏強度
ASTM D-638     23oC kg/cm2 370
Tensile Strength at Break
拉力斷裂強度
ASTM D-638     23oC % 8
Flexural Modulus
彎曲模數
ASTM D-790A     23oC kg/cm2 17000 
Hardness
硬度
ASTM D-785     23oC R-Scale 102
Izod Impact Strength
衝擊強度
ASTM D-256     23oC kg-cm/cm 3
Melting Point
熔點
ASTM D-648 at 4.6kg/cm
Unannealed1/4"
oC 105
Molding Shrinkage
縮收率
FCFC     23oC % 1.3 
Specific Gravity
比重
ASTM D-792    23oC/23oC   0.905

Typical properties can be subject to change without further notice

Polypropylene High Melting Index & Impact
PP 高熔融值耐衝擊
Property
物性
Test Methodbr
測試方式
Unit
單位
Value
數值
Melt Flow Index
熔融指數
ASTM D-1238   230oC x 2.16kg g/10min 15
Tensile Strength at Yield
拉力降伏強度
ASTM D-638     23oC kg/cm2 370
Tensile Strength at Break
拉力斷裂強度
ASTM D-638     23oC % 8
Flexural Modulus
彎曲模數
ASTM D-790A     23oC kg/cm2  17000
Hardness
硬度
ASTM D-785     23oC R-Scale 102
Izod Impact Strength
衝擊強度
ASTM D-256     23oC kg-cm/cm 3
Melting Point
熔點
ASTM D-648 at 4.6kg/cm
Unannealed1/4"
oC 105
Molding Shrinkage
縮收率
FCFC     23oC %  1.3
Specific Gravity
比重
ASTM D-792    23oC/23oC   0.905

Typical properties can be subject to change without further notice